Molybdenum. The all-rounder among the specialists.

 

Molybdenum powder   With its unique mechanical and chemical properties, molybdenum is an outstanding material that can meet the most exacting requirements. Because molybdenum possesses a very high melting point, a low coefficient of thermal expansion and a high level of thermal conductivity, it is used in many different industries.


Molybdenum is a genuine all-rounder. We use this material, for example, to produce ribbons and wires for the lighting industry, semiconductor base plates for power electronics, glass melting electrodes, hot zones for high-temperature furnaces and sputtering targets for coating solar cells and flat screens.

 

Guaranteed purity.

You can rely on our quality. We produce our molybdenum products ourselves – from the metal oxide right through to the finished product. As our input material, we use only the purest molybdenum oxide. This ensures that you benefit from a very high level of material purity. Find out for yourself.

  Specification of Mo

 

 

Go directly to the topic that interests you.

 Applications

 Alloys

    TZM, MHC, ML, MoILQ, MY, MoRe, MoW, MoCu, MoZrO2, MoTa and MoNb

 Properties

   Thermophysical propertiesMechanical properties, Chemical resistance

 Natural occurrence and preparation
 Powder metallurgy

Talented in many areas.

Zum Inhaltsverzeichnis

The industrial applications for our molybdenum are as varied as its properties. We briefly present three of these below:


High purity and excellent creep resistance.

Our molybdenum is exceptionally pure, withstands very high temperatures and is nevertheless still easy to machine. For example,to produce crucibles for all the conventionally employed processes in the field of sapphire growth. Thanks to their exceptional purity, these have proved their worth as optimized melting and solidification vessels.

Formed molybdenum crucible

High dimensional stability and excellent corrosion resistance.

 Molybdenum stirrer  

Our stirrers homogenize all types of glass melt. To do this, they must withstand extreme temperatures and aggressive glass melts. Molybdenum makes it possible. With its excellent dimensional stability and corrosion resistance against metal and glass melts, our material ensures optimum stirring coupled with long product service lives.

 

High thermal conductivity and low thermal expansion.

High power densities and the flow of electricity through power diodes and transistors generate heat. Thanks to its good thermal conductivity and thermal expansion properties that are adapted to the relevant semiconductor material, molybdenum and its alloys are the perfect substrate for power electronics. When used as a base plate, molybdenum reliably dissipates heat.

  Molybdenum base plates

 

Pure molybdenum - or maybe an alloy? It's your choice.

zum Inhaltsverzeichnis 

We prepare our molybdenum to perform perfectly in every application. We can determine the following properties through the addition of various alloys:

  • Physical properties (e.g. melting point, vapor pressure, density, electrical conductivity, thermal conductivity, thermal expansion, heat capacity)
  • Mechanical properties (e.g. strength, fracture behavior, creep resistance, ductility)
  • Chemical properties (corrosion resistance, etchability)
  • Machinability (e.g. cutting processes, formability, weldability)
  • Recrystallization behavior (recrystallization temperature, embrittlement, aging effects)

 

And there's more: By using our own customized manufacturing processes, we can modulate various other properties of molybdenum across a wide range of values. The result: Molybdenum alloys with different ranges of properties which are precisely engineered to meet the requirements of each individual application.

Name of material

Chemical composition
(percentage by weight)
Mo (pure) > 99.97
TZM 0.5 % Ti / 0.08 % Zr / 0.01 - 0.04 % C
MHC 1.2 % Hf / 0.05 - 0.12 % C
Mo-Lanthanoxid (ML) ML 0.3 % La2O3
MLR (R = Recrystallized) 0.7 % La2O3
MLS (S = Stress relieved) 0.7 % La2O3
MoILQ (ILQ = Incandescent Lamp Quality) 0.03 % La2O3
Mo-Yttriumoxid MY 0.47 % Y2O3 / 0.08 % Ce2O3
MoRe MoRe5 5.0 % Re
MoRe41 41.0 % Re
MoW MW20 20.0 % W
MW30 30.0 % W
MW50 50.0 % W
MoCu MoCu30 30.0 % Cu
MoCu15 15.0 % Cu
MoZrO2 MZ17 1.7 % ZrO2
MoTa MT11 11.0 % Ta

TZM (Titanium-Zirconium-Molybdenum).

 zum Inhaltsverzeichnis

We transform our molybdenum into TZM by using small quantities of tiny, extremely fine carbides. TZM is stronger than pure molybdenum and possesses a higher recrystallization temperature and better creep resistance. TZM is used in high-temperature applications involving demanding mechanical loads, for example in forging tools or as rotating anodes in X-ray tubes. The recommended temperatures of use are between 700 and 1 400 °C.

 

  X-ray targets

 

MHC (Molybdenum-Hafnium-Carbon).

MHC is a particle-reinforced molybdenum-based alloy which contains both hafnium and carbon. Thanks to the uniformly distributed, extremely fine carbides, the material benefits from outstanding heat and creep resistance and, at 1 550 °C, the maximum recommended temperature of use is 150 °C higher than that of TZM. MHC is used in metal forming applications, for example. When used in extrusion dies, it is able to withstand extreme thermal and mechanical loads.

  MHC extrusion dies

 

ML (Molybdenum-Lanthanum Oxide).

Small quantities of lanthanum oxide particles (0.3 or 0.7 percent) give the molybdenum a so-called stacked fiber structure. This special microstructure is stable at up to 2 000 °C. Molybdenum-lanthanum oxide is therefore also creep-resistant even under extreme conditions of use. We mostly machine these alloys to produce furnace components such as stranded and other wires, sintering and annealing boats or evaporator coils. In the lighting industry, molybdenum-lanthanum oxide is used, for example, for retaining and feed wires.

  Molybdenum-lanthanum oxide wire

MoILQ (Molybdenum-ILQ).

Zum Inhaltsverzeichnis

MoILQ is a microdoped molybdenum alloy with a lanthanum oxide content of only 0.03 percent by weight which has been specially developed for use in the lighting industry. Thanks to its specially adapted dopant content, its recrystallization temperature is higher than that of pure molybdenum. After recrystallization, its microstructure is also more fine-grained than in the case of pure molybdenum. Compared to our ML material, MoILQ is more suitable for forming and therefore easier to process. MoILQ is used for the core and support wires in the manufacture of filaments for incandescent and halogen lamps.   MoILQ core wire

MY (Molybdenum-Yttrium-Cerium Oxide).

Our MY is a particle-reinforced molybdenum alloy that contains 0.47 percent yttrium oxide by weight and 0.08 percent cerium oxide by weight. We developed MY specially for use in the lighting industry. MY adheres well to quartz glass, is easy to weld and provides better resistance to oxidation than pure molybdenum. MY is primarily used in conductive ESS ribbons and in evaporation boats for applications in the field of coating technology.   Molybdenum-yttrium oxide ESS ribbon 

MoW (Molybdenum-Tungsten).

Tungsten is improved by the high-temperature properties and corrosion resistance of our molybdenum.

 

Available in different compositions from MW20 with 20 percent tungsten by weight to MW50 with 50 percent tungsten by weight, our MoW materials are primarily used for the manufacture of zinc as well as for stirring tools in the glass industry.

 

 

Molybdenum-tungsten target

In addition, we use our MoW alloys to produce sputtering targets for coating flat screens. MoW layers possess enhanced etchability, a property which is of value for the manufacture of thin-film transistors.

MoRe (Molybdenum-Rhenium).

Zum Inhaltsverzeichnis

Small quantities of rhenium make molybdenum ductile even below room temperature. Molybdenum-rhenium (MoRe) is primarily used for thermocouple wires in the standard compositions MoRe5 and MoRe41 as well as in applications where a high level of ductility is important.

MoRe wire

MoCu (Molybdenum-Copper).

Molybdenum-copper (MoCu) is a composite material which contains up to 30 percent copper by weight. This composite combines the high thermal conductivity of copper and the low thermal expansion of molybdenum. Our MoCu is perfect for the manufacture of passive cooling elements (heat sinks and heat spreaders) in electronic components.

 

Due to their low weight, molybdenum-copper composites are particularly suitable for this type of application where every gram counts: In the automotive industry they are used as carrier plates for the IGBT modules that act as inverters in electric drives.

 

Molybdenum-copper heat sinks 

MoZrO2 (Molybdenum-Zirconium Oxide).

Zum Inhaltsverzeichnis

Glass melting electrodes must withstand aggressive glass melts and very high temperatures. By adding 1.7 percent zirconium oxide by weight, we have endowed our molybdenum with properties that are of particular value for the glass industry. MoZrO2 offers better corrosion resistance against glass melts, greater stability at high temperatures and better creep resistance than pure molybdenum.    Molybdenum-zirconium oxide glass melting electrodes

MoNb (Molybdenum-Niobium).

Our molybdenum sputtering targets are used to produce thin functional layers for flat screens. In the case of touch panels, in particular, a high level of corrosion resistance is essential. We therefore add the alloy element niobium to our all-round star, molybdenum, in order to achieve a particularly high level of corrosion resistance.
Get more details on MoNb sputtering targets.

 

MoTa (Molybdenum-Tantalum).

You want to combine high corrosion resistance and easy structuring of the sputtered layer? Then we recommend our MoTa alloy

 Molybdenum-tantalum target

A good all-rounder. Material properties of molybdenum.

Zum Inhaltsverzeichnis

Molybdenum belongs to the group of refractory metals. Refractory metals are metals that have a higher melting point than platinum (1 772 °C). In refractory metals, the energy binding the individual atoms together is particularly high. Refractory metals have a high melting point coupled with a low vapor pressure, high modulus of elasticity and high thermal stability. Refractory metals are also typically characterized by a low coefficient of thermal expansion and relatively high density.

 

The fact that molybdenum belongs to the same group as tungsten in the periodic table means that it has a similar atomic structure and chemical properties. The excellent thermal conductivity of both molybdenum and tungsten is also of particular interest. However, molybdenum is easily deformable even at quite low temperatures and is therefore simpler to work than tungsten.

 

Molybdenum is a genuine all-rounder with a very well-balanced range of properties:

 

Properties
Atomic number 42
Atomic mass 95.94
Melting point 2 620 °C / 2 893 K
Boiling point 5 560 °C / 5 833 K
Atomic volume 1.53 · 10-29 [m3]

Vapor pressure

at 1 800 °C 1 · 10-4 [Pa]
at 2 200 °C · 10-2 [Pa]
Density at 20 °C (293 K) 10.2 [g/cm3]
Crystal structure body-centred cubic
Lattice constant 3.147·10-10 [m]

Hardness at 20 °C (293 K)

stress-relief annealed > 220 [HV10]
recrystallized 160 - 180 [HV10]
Modulus of elasticity at 20 °C (293 K) 320 [GPa]
Poisson number 0.31
Coefficient of linear thermal expansion at 20 °C (293 K) 5.2 · 10-6 [m/(m·K)]
Thermal conductivity at 20 °C (293 K) 142 [W/(m·K)]
Specific heat at 20 °C (293 K) 0.254 [J/(g·K)]
Electrical conductivity at 20 °C (293 K) 17.9 · 106 [1/(Ω·m)]
Specific electrical resistance at 20 °C (293 K) 0.056 [(Ω·mm2)/m]

Sound speed at 20 °C (293 K)

Longitudinal wave 6 250 [m/s]
Transverse wave 3 350 [m/s]
Electron work function 4.39 [eV]
Capture cross-section for thermal neutrons 2.7 · 10-28 [m2]

 

We are able to influence the properties of our molybdenum and its alloys by varying the type and quantity of alloy elements that we add as well as by using tailor-made production processes.

 

The carbides that we specifically include in our TZM and MHC materials modulate the mechanical properties of molybdenum across all temperature ranges. In particular, oxides increase the recrystallization temperature and creep resistance of the molybdenum. Rhenium makes molybdenum ductile even at room temperature. Copper increases the thermal conductivity without having any serious effects on the coefficient of expansion.

 

Mo TZM MHC ML

Alloy components

(percentage by weight)

99.97 % Mo

0.5 % Ti / 0.08 % Zr

0.01 - 0.04 % C

1.2 % Hf

0.1 % C

0.3 % La2O3

0.7 % La2O3

Thermal conductivity

- -

Stability at room temperature

~ + +

Stability at high temperature

++
(< 1 400 °C)
++
(< 1 500 °C)
+
(> 1 400 °C)
Creep resistance

+

(>1 400 °C)

+

(<1 500 °C)

++

(<1 400 °C)

Recrystallization temperature

+ ++ ++
Ductility after HT use + + ++
Weldability + + +

 

 

MoILQ MY MoW MoRe MoCu

Alloy components

(percentage by weight)

0.03 %

La2O3

0.47 % Y2O3

0.08 % Ce2O3

20 - 50 %

W

5 / 41 % Re

15 - 30 %

Cu

Thermal conductivity ~ ~ - - ++
Stability at room temperature ~ ~ + + -

Stability at high temperatures

+ + + + -

Creep resistance

+ + + + -
Recrystallization temperature + + + +

-

Ductility + + ~ ++

+

Weldability + + ~ ++

-

 

~ comparable with pure Mo + higher than pure Mo ++ much higher than pure Mo - lower than pure Mo -- much lower than pure Mo

 

Thermophysical properties.   

Zum Inhaltsverzeichnis

Refractory metals are typically characterized by a low coefficient of thermal expansion and relatively high density. The same is true of molybdenum. This material is also characterized by a high level of thermal conductivity and low electrical specific resistance. Molybdenum atoms are strongly bonded and the element has a higher modulus of elasticity than many other metals.
 
The thermophysical properties of molybdenum change with temperature. The diagrams below indicate the curves of the most important variables compared to tungsten:

 

Coefficient of linear thermal expansion of molybdenum

Coefficient of linear thermal expansion of molybdenum and tungsten

 

 

 Specific heat capacity of molybdenum
 Specific heats of molybdenum and tungsten

 

The specific electrical resistivity of a material is the multiplicative inverse of its electrical conductivity. The lower the value of the specific electrical resistivity of a material, the better is its conduct current. The specific electrical resistivity is measured in Ωmm²/m. Metals show very different specific electrical resistivities. An example: silver 0.016 Ωmm²/m; titanium 0.8 Ωmm²/m. The temperature, alloying elements, impurities and defects of the respective material strongly influence the specific electrical resistivity. Our high performance materials molybdenum and tungsten show a very low specific electrical resistivity: appr. 0.05 Ωmm²/m at room temperature and even less then 0,5 Ωmm²/m at a temperature of 1,500°C. Therefore our metals are best suitable for the use as contact and coating materials. As molybdenum and tungsten have a cubic crystallattice, the specific electrical resistivity shows the same value in all crystallographic orientations.

 Specific electrical resistance
 Specific electrical resistance of molybdenum and tungsten

 

 

 Thermal conductivity of molybdenum

 

Thermal conductivity of molybdenum and tungsten as a function of temperature

Mechanical properties

Zum Inhaltsverzeichnis

 
Due to its high melting point of 2 620 °C, molybdenum retains its strength and creep resistance even at high temperatures. The strength of molybdenum increases even further the more the material is cold-worked. In contrast to that of other metals, the ductility of molybdenum materials also increases with increasing cold working. We add rhenium as an alloy element to increase the ductility of molybdenum and to reduce its brittle-ductile transition temperature. We also use titanium, zirconium, hafnium, carbon and oxides of rare earths as alloy components to add to our molybdenum. Compared to other metals, the modulus of elasticity of molybdenum and its alloys is very high due to the strong bonds between the molybdenum atoms. This means that we are able to create a variety of materials with very specific ranges of properties.

 

Modulus of elasticity of molybdenum

 

Modulus of elasticity of molybdenum plotted against the testing temperature compared to our other refractory metals: tungsten, tantalum and niobium.

Transition temperature

Brittle-to-ductile transition temperature

If molybdenum is heated above a certain temperature then it loses its brittleness and becomes ductile. This temperature that is required to bring about the transition from brittleness to ductility is known as the brittle-to-ductile transition temperature. It depends on various factors including the chemical composition and level of cold working of the metal.

The ductility and fracture toughness of molybdenum materials decrease as the recrystallization level increases. This means that the recrystallization temperature is a decisive factor. Above the recrystallization temperature, the structure of the material changes. This restructuring of the grain reduces the strength and hardness of molybdenum and increases the likelihood of fractures. Demanding forming processes such as rolling, swaging or drawing are necessary in order to restore the initial structure.

 

The recrystallization temperature is highly dependent on the level of cold working of the molybdenum and on its chemical composition, and in particular its dopant content. The table below summarizes the typical recrystallization temperatures of basic molybdenum materials.


Material Temperature [°C] for 100 % recrystallization (annealing time: 1 hour)

Deformation level = 90 %

Deformation level = 99.99 %
Mo (pure) 1 100 -
TZM 1 400 -
MHC 1 550 -
ML 1 300 2 000
MoILQ 1 200 1 400
MY 1 100 1 350
MoRe41 1 300 -
Mo30W 1 200 -

 

During the forming and machining of molybdenum and refractory metals in general, it is important to possess a good understanding of the special properties of this group of materials. If forming processes such as bending or folding are used, then these must be employed above the brittle-ductile transition temperature to ensure that the sheet can be safely worked without risk of fissuring. The thicker the sheet, the higher the temperature that is required for fissure-free forming. Molybdenum is also perfectly suited for cutting and punching operations provided that the tool is properly sharpened and the preheating temperature is correctly adjusted. However, cutting processes can also be performed without problem at extremely robust, powerful machines. If you have any special questions relating to the forming and machining of refractory metals, we would be glad to assist you with our many years of experience.

Chemical resistance.

Zum Inhaltsverzeichnis

 

The excellent chemical resistance of molybdenum and its alloys is particularly appreciated in the chemicals and glass industries. At an atmospheric humidity of under 60 %, molybdenum is corrosion-resistant. Only at higher levels of humidity does discoloration start to occur. In alkaline and oxidizing liquids, molybdenum loses its resistance at temperatures of over 100 °C. For applications in which molybdenum is used in oxidizing gases and elements at over 250 °C, we have developed the SIBOR® protective layer to prevent oxidation. Glass melts, hydrogen, nitrogen, noble gases, metal melts and oxide ceramics do not attack molybdenum even at very high temperatures or have a less aggressive effect than they do on other metallic materials. 

 

The table below indicates the corrosion resistance of molybdenum. Unless indicated to the contrary, the specifications relate to pure solutions not mixed with oxygen. Tiny concentrations of extraneous chemically active substances can significantly affect the corrosion resistance. Do you have any questions regarding complex corrosion-related topics? We would be delighted to help you with our experience and our in-house corrosion laboratory.

 

Corrosion resistance of molybdenum
Water Cold and warm water < 80 °C (353 K) resistant
Hot water > 80 °C (353 K) not resistant
Hot water with nitrogen gassing or inhibitor resistant
Inorganic acids Hydrofluoric acid < 100 °C (373 K) resistant
Nitrohydrochloric acid, cold and warm not resistant
Orthophosphoric acid up to 270 °C (543 K) resistant
Nitric acid, cold and warm not resistant
Hydrochloric acid, cold and warm resistant
Sulfuric acid < 70 % up to 190 °C (463 K) resistant
Chromosulfuric acid not resistant
Lyes Ammonia solution resistant
Potassium hydroxide (KOH < 50 %) up to 100 °C (373 K) resistant
Potassium hydroxide (KOH > 50 %) not resistant
Sodium hydroxide (NaOH < 50 %) up to 100 °C (373 K) resistant
Sodium hydroxide (NaOH > 50 %) not resistant
Sodium hypochlorite solution, cold and warm not resistant
Organic acids Formic acid 20 °C (293 K) resistant
Acetic acid up to 100 °C (373 K) resistant
Conc. lactic acid 20 °C (293 K) resistant
Oxalic acid 20 °C (293 K) resistant
Tartaric acid 20°C (293 K) resistant
Non-metals Boron up to 1 600 °C (1 873 K) resistant
Carbon up to 1 100 °C (1 373 K) resistant
Phosphorous up to 800 °C (1 073 K) resistant
Sulfur up to 440 °C (713 K) resistant
Silicon up to 600 °C (873 K) resistant
Fluorine 20 °C (293 K) not resistant
Chlorine up to 250 °C (523 K) resistant
Bromine up to 450 °C (723 K) resistant
Iodine up to 450 °C (723 K) resistant
Glass melts* Up to 1 700 °C (1 973 K) resistant

 

* Excluding glasses containing oxidants (e.g. lead glass)

Zum Inhaltsverzeichnis

Corrosion resistance against gases
Ammonia gas resistant at < 1 000 °C

Air and oxygen

resistant at < 400 °C
Noble gases no reaction Nitrogen no reaction
Carbon dioxide resistant at < 1 200 °C Hydrogen no reaction
Carbon monoxide resistant at < 1 400 °C Water vapor resistant at < 700 °C
Hydrocarbons resistant at < 1 100 °C

 

Please note that in atmospheres containing oxygen, in particular, a high level of oxidation occurs at temperatures over 400 °C. With special coatings such as SIBOR®, we prevent the oxidation of molybdenum.

 

Corrosion resistance against ceramic furnace construction materials
Aluminum oxide resistant at < 1 900 °C

Magnesium oxide

resistant at < 1 600 °C
Beryllium oxide resistant at < 1 900 °C Silicon carbide resistant at < 1 300 °C
Graphite resistant at < 1 100 °C Zirconium oxide resistant at < 1 900 °C
Magnesite bricks resistant at < 1 600 °C

 

The addition of up to 30 percent by weight of tungsten as an alloy component significantly improves the corrosion resistance of molybdenum, for example in zinc.

 

Corrosion resistance against metal melts
Aluminum resistant at < 700 °C Sodium resistant at < 1 030 °C
Beryllium not resistant Nickel not resistant
Lead resistant at < 1 100 °C Plutonium resistant at < 900 °C
Oxygen-containing
lead
resistant at < 500 °C Mercury resistant at < 600 °C
Caesium resistant at < 870 °C Rubidium resistant at < 1 000 °C
Iron not resistant Scandium not resistant
Gallium resistant at < 300 °C Rare earths resistant at < 1100 °C
Potassium resistant at < 1200 °C Silver resistant
Copper resistant at < 1300 °C Uranium not resistant
Gold resistant Bismuth resistant at < 1400 °C
Lithium resistant at < 1400 °C  Zinc  resistant at < 400 °C
Magnesium resistant at < 1000 °C Tin  resistant at < 550 °C

Natural occurrence and preparation.

Zum Inhaltsverzeichnis

Molybdenum has been known since the 3rd century BC. However, at that time, the term "molybdaena" was used to refer to graphite and galena which was confused with (naturally occurring) molybdenite. It was not until the 17th century that scientists realized that molybdaena had no lead content, and in 1778, Carl Wilhelm Scheele used nitiric acid to produce white molybdenum oxide (MoO3). Scheele named the white precipitate "terra molybdaenae" (molybdenum earth).

 

In 1781, Peter Jakob Hjelm succeeded in reducing molybdenum oxide for the first time. The result: Metallic molybdenum. However, we have Jöns Jakob Berzelius to thank for the chemical symbol and our knowledge of the chemical properties of molybdenum. Pure molybdenum was produced for the first time at the beginning of the 20th century by reducing molybdenum trioxide (MoO3) with hydrogen.

 

The most important minerals used for the manufacture of molybdenum are molybdenite (MoS2). The world's largest molybdenum reserves can be found in North and South America and China. In the copper mines of Chile, molybdenite is extracted as a by-product of the country's copper mining operations.

 

These ores have a molybdenum content of approximately 0.5 percent by weight. The accompanying minerals are separated from the molybdenum using the so-called flotation process. After being subjected to this method, the concentrate contains on average approximately 85 % molybdenite (MoS2). This concentrate is roasted at 600 °C. The molybdenite (MoS2) is oxidized to form molybdenum trioxide (MoO3).

 

 

With our holding in the Chilean company Molibdenos y Metales (Molymet) we have made an important step towards safeguarding our long-term supply of molybdenum. Molymet is the world's largest processor of molybdenum ore concentrates.

 

MOLYMET

Fact Box
Did you know that molybdenum concentrate contains approximately 0.1 % rhenium? During the roasting process, this rhenium is sublimated as rhenium heptoxide (Re2O7) and is retrieved in the dust separator as a by-product of the molybdenum preparation process.
The roasted molybdenum concentrate, or molybdenum oxide as it is technically known, is sublimated at approximately 1 000 °C or is cleansed even further using chemical methods. This process yields the following products for the manufacture of metallic molybdenum:

 

ADM (ammonium dimolybate) (NH4)2O 2MoO3 white
Molybdenum trioxide MoO3 green

 

 

We then subject the above-mentioned intermediate products to a two-stage reduction process in the presence of hydrogen in order to obtain metallic molybdenum powder. We reduce molybdenum trioxide in a hydrogen atmosphere to obtain a slightly reduced molybdenum oxide (MoO2) which has a typical reddy-brown color. As a result, molybdenum oxide is also known as "molybdenum red":

 

Reduction of molybdenum trioxide

The second reduction is also performed in a hydrogen atmosphere and results in the end product – a metallic grey molybdenum powder:
 

 

Reduction of molybdenum dioxide

How do we do it? With powder metallurgy!

Zum Inhaltsverzeichnis

So what is powder metallurgy? It is well known that nowadays most industrial metals and alloys, such as steels, aluminum and copper, are produced by melting and casting in a mold. In contrast, powder metallurgy does away with the melting operation and the products are manufactured by compacting metal powders which are then subjected to a heat treatment (sintering) below the melting temperature of the material. The three most important factors in the field of powder metallurgy are the metal powder itself as well as the compacting and sintering operations. We are able to control and optimize all these factors in-house.

 

Why do we use powder metallurgy? Powder metallurgy allows us to produce materials with melting points of well over 2 000 °C. The procedure is particularly economical even when only small quantities are produced. In addition, by using tailor-made powder mixes, we can produce a range of extremely homogeneous materials endowed with specific properties.

 

The molybdenum powder is mixed with the possible alloy elements and then filled into molds. The mixture is then compacted at pressures of up to 2 000 bars. The resulting pressed part (also known as a "green compact") is then sintered in special furnaces at temperatures of over 2000 °C. During this process, the part acquires its density and its microstructure forms. The very special properties of our materials - such as their excellent thermal stability, their hardness or their flow characteristics - are due to the use of the appropriate forming methods, for example forging, rolling or drawing. Only when all these steps dovetail perfectly can we achieve our exacting quality demands and manufacture products of outstanding purity and quality.
 

 

 

Raw material Reduction Metal powder Mixing Pressing Sintering Forming Heat treatment Machining-Joining-Coating Quality assurance


Raw material
(oxide)


Reduction


Metal
powder


Mixing


Pressing


Sintering


Forming


Heat
treatment 


Machining
Joining
Coating 


Quality
assurance

 

Molybdenum

 

Atomic number

42

CAS number

7439-98-7

Atomic mass

95.94

Melting point

2 893 K
2 620 °C

Boiling point

5 833 K
5 560 °C

Atomic volume

0.0153 [nm3]

Density at 20 °C

10.2 [g/cm3]

Crystal structure

body-centered cubic

Lattice constant

0.3147 [nm]

Abundance in the Earth's crust

1.2 [g/t]

You can download our safety data sheets here.

 

   Mo, TZM, MHC, ML, MY (engl.)

 

   MoRe (engl.)

 

   MoW (engl.)

 

   MoCu (engl.)

 

   MoTa (engl.)

 

 

Sheets 

Ribbon 

Rods

Furnace parts 

Shop right now!

plansee.com RSS-Feed
Follow our RSS feed
Recommend this page